Color variation of composite resins in relation to the Vita Classical shade guide: colorimetric analysis

Aim: The aim of this study was to verify the color variation between different composite resins and the Vita Classical Shade Guide. Methods: Two-millimeter thickness samples were made (n = 6) from eight commercial brands of composite resin (shade A2): Charisma (Kulzer), Forma (Ultradent), Harmonize (Kerr), Luna (SDI), Opallis (FGM), Oppus Bulk Fill (FGM), Vittra (FGM) and Filtek Z250 XT (3M ESPE). Specimens were stored in distilled water for 7 days and then polished. Color measurements of samples and A2 shade of the Vita Classical Shade Guide were performed using the Vita Easy Shade Advance 4.0 spectrophotometer on a black background. Color variations were calculated using the CIEDE2000 formula, considering values ≥0.81 being noticeable by the human eye and ≥1.77 being clinically unacceptable. Results were statistically analyzed with a 5% significance level. Results: Color variation (ΔE) of composite (E1 ) compared to the Vita Classical Shade Guide (E0 ) was greater than clinically acceptable for all the materials evaluated in this study. Forma (ΔE=2.08 ± sd=0.47) and Filtek Z250 XT (2.50 ± 0.20) had the smallest amount of color variation values found in the results. Harmonize (3.32 ± 0.63) presented values similar to Filtek Z250 XT, but it was worse than Forma. Vittra (3.51 ± 0.28), Charisma (3.80 ± 0.20), Opallis (4.24 ± 0.30) and Luna (5.67 ± 0.20) did not differ among each other and presented higher color variation than Forma, Filtek Z350XT and Harmonize. Oppus Bulk Fill (13.94 ± 1.12) was the composite with the greatest color variation. Conclusions: The findings in this study show that attention should be taken when using the Vita Color Shade Guide for composite shade selection

Envelhecimento bucal precoce e suas consequências para a cavidade oral com foco em reabilitação com resina composta: relato de caso / Early oral aging and its consequences for the oral cavity focusing on rehabilitation with composite resin: case report

O envelhecimento bucal precoce apresenta cada vez uma maior incidência nos consultórios odontológicos e sua degradação aos tecidos orais exige uma atenção por parte do cirurgiãodentista devido ao seu alto grau de complexidade. Esse envelhecimento precoce é causado principalmente por hábitos parafuncionais, dieta ou ambos. Suas consequências são desgastes patológicos dos tecidos dentários, extrusão passiva, perda de dimensão vertical e comprometimento estético e funcional. Por conta disso, o presente estudo teve como objetivo realizar um relato de caso clínico em um paciente jovem e com queixa estética como consequência de hábitos parafuncionais, aonde foram realizados uma reabilitação oral envolvendo aumento da dimensão vertical de oclusão através de Table Tops sem desgastes dentários e restaurações estéticas, ambas com resina composta. Essa reabilitação devolveu a DVO da paciente, trazendo conforto, contatos estáveis, guias de desoclusão e satisfação estética e funcional por parte da paciente(AU)

Early oral aging has an increasing incidence in dental offices and its degradation to oral tissues requires attention from the dentist due to its high degree of complexity. This premature aging is mainly caused by parafunctional habits, diet, or both. Its consequences are pathological wear of dental tissues, passive extrusion, loss of vertical dimension and aesthetic and functional impairment. Because of this, the present study aims to carry out a clinical case report in a young patient with an aesthetic complaint as a result of parafunctional habits, where an oral rehabilitation was carried out involving an increase in the vertical dimension of occlusion through Table Tops without dental wear and aesthetic restorations, both with composite resin. This rehabilitation returned the patient's OVD, bringing comfort, stable contacts, disocclusion guides and aesthetic and functional satisfaction on the part of the patient(AU)

Degree of Conversion and Mechanical Properties of a Commercial Composite with an Advanced Polymerization System / Avaliação do grau de conversão e das propriedades mecânicas de um compósito comercial com sistema avançado de polimerização

ABSTRACT Advanced Polymerization System (APS) technology in a commercial composite resin enables reduction of the concentration of camphorquinone without altering composite physicochemical properties. Aim: The aim of this study was to evaluate the degree of conversion and mechanical properties of a commercial composite with an advanced polymerization system (APS) and compare it to other composites that do not use this system. Materials and Method: Five groups were analyzed. Group 1 (VT: Vittra APS - FGM); G2 (AU: Aura - SDI); G3 (ES: Quick Sigma Stelite - TOKOYAMA); G4 (FZ: Filtek Z350 XT - 3M ESPE); G5 (OP: Opallis -FGM). Degree of conversion (DC, n=3) was analyzed immediately and after 24h by analysis with FTIR spectroscopy. For Knoop hardness (KHN, n=3), 5 indentations were made at the top and bottom of specimens 2 mm thick. Flexural strength (FS, n=10) was determined by the three-point method in a universal testing machine. Polymerization stress (PS) was determined by light-curing the material (1.0 mm high) between polymethylmethacrylate rods in a universal testing machine. Light curing was performed with a Valo Cordless LED (1,000 mW/cm2 x 20 s: 20J). The results were analyzed using ANOVA and complemented by Tukey's test (α=0.05). Results: The highest DC values (immediate and 24h after) were observed for VT and OP resins, followed by FZ, AU and ES. FZ (top and bottom) had the highest KHN values, similar to VT top. AU, ES, OP and VT had statistically different KHN between their top and bottom surfaces. The highest RF values were observed for FZ, followed by OP/VT, ES and AU. The highest TP values were observed for FZ, OP and VT. Conclusion: The Vittra APS resin with a new polymerization system presents satisfactory performance for the parameters evaluated.

RESUMO A tecnologia Advanced Polymerization System (APS) presente em uma resina composta comercial permite reduzir a concentração de canforoquinona sem alterar as propriedades físico-químicas do compósito. Objetivo: o objetivo deste estudo foi avaliar o grau de conversão e as propriedades mecânicas de um compósito comercial com sistema avançado de polimerização (SAP) e comparálo com outros compósitos que não utilizam esse sistema. Materiais e Método: cinco grupos foram analisados. Grupo 1 (VT: Vittra APS - FGM); G2 (AU: Aura - SDI); G3 (ES: Quick Sigma Stelite - TOKOYAMA); G4 (FZ: Filtek Z350 XT - 3M ESPE); G5 (OP: Opallis -FGM). O grau de conversão (GC, n=3) foi analisado imediatamente e após 24h através da análise com espectroscopia FTIR; para dureza Knoop (DK, n=3), foram feitas 5 indentações no topo e na base de corpos de prova de 2 mm de espessura; para determinar a resistência à flexão (RF, n=10), o método de três pontos foi realizado em uma máquina universal de ensaios; a tensão de polimerização (TP) foi determinada pela fotopolimerização do material (1,0 mm de altura) entre hastes de polimetilmetacrilato em uma máquina de teste universal. A fotopolimerização foi realizada com um Valo Cordless LED (1.000 mW/cm2 x 20 s: 20J). Os resultados foram analisados por ANOVA e complementados pelo teste de Tukey (α=0,05). Resultados: os maiores valores de GC (imediato e 24h após) foram observados para as resinas VT e OP, seguidas de FZ, AU e ES. A resina FZ (superior e inferior) apresentou os maiores valores de DK, semelhante ao VT superior. As resinas AU, ES, OP e VT apresentaram DK estatisticamente diferente entre suas superfícies de topo e base. Os maiores valores de RF foram observados para FZ, seguido de OP/VT, ES e AU. Os maiores valores de TP foram observados para FZ, OP e VT. Conclusão: com base nos resultados, pode-se concluir que a resina Vittra APS com um novo sistema de polimerização apresenta desempenho satisfatório para os parâmetros avaliados.

Facetas diretas em resina composta utilizando o fluxo digital para planejamento: relato de caso / Direct facets in composite resin using digital flow for planning: case report / Facetas directas en resina compuesta utilizando flujo digital para planificación: reporte de caso

Introdução:O aprimoramento das resinas compostas nos últimosanos em associação com a difusão de informações nas redes sociais tornou as facetas diretas tratamentos populares na dentística restauradora. No entanto, são procedimentos que exigem ampla destreza manual e conhecimento técnico. O fluxo digital através doescaneamento, enceramento digital e prototipagem 3D para construção de guias tem se tornado uma excelente alternativa para aumentar a previsibilidade e aumentar a longevidade destes trabalhos. Objetivo:Descrever o protocolo de confecção de facetas diretas em resina composta, através de um relato de caso, utilizando como auxílio o planejamento digital para confecção de modelo 3D, guia de silicone e paredes palatinas. Descrição do Caso:Paciente do gênero masculino, 43 anos, queixava-se do formato dos seus dentes. Ao exame clínico percebeu-se desgaste dental nos incisivos centrais e linha do sorriso levemente invertida. Após duas sessões de clareamento de consultório com Peróxido de hidrogênio (35%) e mockup direto com resina composta, foi realizada a moldagem e escaneamento do modelo de gesso no laboratório. O enceramento digital foi aprovado, o modelo 3D foi impresso para confecção da guia de silicone. Com auxílio da guia foram executadas facetas diretas nos elementos 13, 12, 11, 21, 22 e 23. Conclusão:O fluxo digital pode ser uma alternativa viável para minimizar as falhas na confecção de facetas diretas em resina composta (AU).

Introduction:The improvement of composite resins in recent years, together with information disseminated on social media, has made direct veneers popular treatments in restorative dentistry. However, these procedures require significant manual dexterity and technical knowledge. Digital work flow using scanning, digital wax-up and 3D prototyping for the construction of guides has become an excellent alternative to increase predictability and the longevity of these procedures. Objective:Describe the manufacturing protocol for direct composite resin veneers, using a case report and digital to construct the 3D model, silicone guide and palatine walls. Case description:Male patient, 43 years old, complained of the shape of his teeth. Clinical examination revealed tooth wear on the central incisors and a slightly inverted smile line. After two whitening sessions with hydroigen peroxide (35%) and direct mockup with composite resin, the plaster model was molded and scanned in the laboratory. Digital wax-up was approved, and the 3D model was printed to manufacture the silicone guide. With the help of the guide, the direct veneers were applied to elements 13, 12, 11, 21, 22 and 23.Conclusions:Digital flow may be a feasible alternative to minimize manufacturing flaws in direct composite resin veneers (AU).

Introducción: La mejora de las resinas compuestas en los últimos años, y la difusión de información en las redes sociales, ha popularizado las facetas directas en los tratamientos en odontología restauradora. Sin embargo, son procedimientos que requieren demasiado destreza manual y conocimientos técnicos. El flujo digital usando escaneo, encerado digital y prototipado 3D para la construcción de guías se ha convertido en una excelente alternativa para aumentar la previsibilidad y la longevidad de estos procedimientos. Objetivo: Describir el protocolo para la realización de carillas directas en resina compuesta, a través de un reporte de caso, utilizando el planeo digital como ayuda para la realización de un modelo 3D, guía de silicona y paredes palatinas. Descripción del caso: Paciente masculino, 43 años, se quejó de la forma de sus dientes. El examen clínico reveló desgaste dental en los incisivos centrales y una línea de sonrisa levemente invertida. Después de dos sesiones de blanqueamiento en consultorio con peróxido de hidrógeno (35%) y maqueta directa con resina compuesta, el modelo de yeso fue moldeado y escaneado en el laboratorio. El encerado digital fue aprovado, el modelo 3D fue impreso para hacer la guía de silicona. Con la ayuda de la guía se realizaron carillas directas en los elementos 13, 12, 11, 21, 22 y 23. Conclusiones: El fluxo digital puede ser una alternativa viable para minimizar fallas en la fabricación de carillas directas en resina compuesta (AU).

Reabilitação estética e funcional com resina composta após trauma dentário: relato de caso / Aesthetic and functional rehabilitation with composite resin after dental trauma: case report

As lesões dentárias traumáticas são um problema de saúde pública mundial, dentre as quais a fratura dentária é a de maior ocorrência, envolvendo principalmente os dentes anteriores. A abordagem de grandes fraturas anteriores é um desafio para cirurgiões dentistas de qualquer nível pois, além da função, afetam diretamente a estética do paciente, fazendo-se necessário um planejamento que envolva diferentes especialidades na odontologia. Objetivo: Relatar um caso clínico de reabilitação funcional e estética de fratura dentária nos incisivos centrais superiores envolvendo tratamento endodôntico, instalação de pino de fibra de vidro e restauração direta em resina composta. Relato de Caso: O paciente de 17 anos sofreu fratura nos incisivos centrais superiores causada por uma queda de bicicleta. Devido à busca tardia por tratamento o elemento 21 foi diagnosticado com necrose pulpar e, portanto, foi submetido à tratamento endodôntico pela Técnica Crown Down e reabilitação com pino de fibra de vidro Splendor-SAP. Posteriormente, os elementos 11 e 21 foram restaurados com facetas diretas em resina composta pela técnica incremental. Conclusão: A reabilitação com instalação de pino de fibra de vidro associada à técnica de estratificação incremental em resina composta se mostra como uma boa opção para reabilitação estética pois permite dar forma anatômica ao dente com riqueza de detalhes na estratificação da dentina e esmalte, além de máxima preservação da estrutura dental. Os resultados obtidos reforçam o sucesso estético e funcional com significativo impacto na qualidade de vida do paciente(AU)

Traumatic dental injuries are a worldwide public health problem, among which dental fractures are the most frequent, mainly involving the anterior teeth. The approach of large anterior fractures is a challenge for dental surgeons of any level because, in addition to function, they directly affect the patient's esthetics, requiring a plan that involves different specialties in dentistry. Objective: Report a clinical case of functional and aesthetic rehabilitation of dental fractures in maxillary central incisors involving endodontic treatment, installation of a fiberglass post and direct restoration in composite resin. Case Report: The 17-year-old patient suffered a fracture in the upper central incisors caused by a fall from a bicycle. Due to the late search for treatment, element 21 was diagnosed with pulp necrosis and, therefore, underwent endodontic treatment using the Crown Down Technique and rehabilitation with a Splendor-SAP fiberglass pin. Later, elements 11 and 21 were restored with direct veneers in composite resin using the incremental technique. Conclusion: Rehabilitation with the installation of a fiberglass post associated with the incremental layering technique in composite resin is a good option for aesthetic rehabilitation as it allows the anatomical shape of the tooth with rich details in the layering of dentin and enamel, in addition to maximum preservation of the tooth structure. The results obtained reinforce the aesthetic and functional success with a significant impact on the patient's quality of life(AU)

In vitro comparison of marginal infiltration between a conventional resin and a bulk-fill resin, in the relocation of cervical margins technique / Comparación in vitro de la infiltración marginal entre una resina convencional y una resina bulk-fill, en la técnica de reubicación de márgenes cervicales

Introduction: Proximal lesions that exceed the cement enamel limit (ACE) under the gingival margin complicate impressions and the adhesive technique. Compare the magnitude of micro infiltration between conventional resin and bulk fill resin in the cervical margin relocation technique. Materials and Methods: 48 samples of human teeth re-ceived two preparations: occluso-mesial (OM) and occluso-distal (OD) under LAC; first they received the cervical margin relocation technique (RMC) with bulk fill and conventional resin; then restored with semi-direct resinous inlays. Sample analysis: immersion in 50% colloidal silver nitrate solution, 24 hours, 37°C and cut mesiodistally. Observed under a stereoscopic magnifying glass to assess dye penetration and digitally photographed, analyzed with "Image J" software. Results: Sample of 96 cavities in two groups of 48 units; control group restored with conventional resin with incremental technique and study group restored with bulk fill resin, mono-incremental technique. Probabilistic sampling. No statistically significant diffe-rences in percentage of microinfiltrated area between Filtek™ Z250™ and Filtek™ Bulk Fill™ (p-value= 0.68). Discussion: Various studies show that the presence of marginal microinfiltration exist independent of: restorative technique, consistency, adhesive mechanism and polyme-rization technique. The research carried out is no exception, observing a similar degree for both systems. Conclusions: Results allow us to conclude that conventi-onal resin and bulk fill resin did not show significant differences in microleakage percentages for the RMC technique. Outside the study framework, bulk fill resins would have comparative advantages; better behavior against light in depths greater than 2 mm, less sensitivity to the "C" factor, and less clinical time.

Introducción: Las lesiones proximales que superan el límite cemento esmalte (ACE) por debajo del margen gingival complican las impresiones y la técnica adhesiva. Comparar la magnitud de la microinfiltración entre la resina convencional y la resina de relleno en la técnica de reubicación del margen cervical. Materiales y Métodos: 48 muestras de dientes humanos recibieron dos preparaciones: ocluso-mesial (OM) y ocluso-distal (OD) bajo LAC, primero recibieron la técnica de reubicación del margen cervical (RMC) con relleno en bloque y resina convencional; luego restaurado con incrustaciones resinosas semidirectas. Análisis de la muestra: inmersión en solución de nitrato de plata coloidal al 50%, 24 horas, 37°C y corte mesiodistal. Observado bajo una lupa estereoscópica para evaluar la penetración del tinte y fotografiado digitalmente, analizado con el software "Image J". Resultados: Muestra de 96 cavidades en dos grupos de 48 unidades; grupo control restaurado con resina convencional con técnica incremental y grupo estudio restaurado con resina bulk fill, técnica mono-incremental. Muestreo probabilístico. No hubo diferencias estadísticamente significativas en el porcentaje de área microinfiltrada entre Filtek™ Z250™ y Filtek™ Bulk Fill™ (p-value = 0,68) Discusión: Diversos estudios evidencian presencia de microinfiltración marginal, independiente de técnica restauradora, consistencia, mecanismo adhesivo y técnica polimerizadora. La investigación realizada no es excepción, observándose grado similar para ambos sistemas. Conclusiones: Los resultados permiten concluir que resina convencional y resina bulk fill no presentaron diferencias significativas en porcentajes de microinfiltración para técnica RMC. Fuera del marco del estudio, resinas bulk fill tendrían ventajas comparativas; mejor comportamiento frente a la luz en profundidades superiores a 2 mm, menor sensibilidad al factor "C", y menor tiempo clínico.

Effects of applying procyanidins on the bond strength of bleached dentin to composite resin / 口腔疾病防治

Objective@#To study the influence of procyanidins on the bonding strength of dentin bleached by carbamide peroxide to composite resin.@*Methods @#By applying different treatments to dentin bonding interfaces, 120 human third molars were randomly divided into 12 groups (n = 10): W group (no bleaching+deionized water), Wa group (no bleaching+deionized water+aging), WT1 group (no bleaching+5% procyanidins for 1 min), WT1a group (no bleaching+5% procyanidins for 1 min+aging), WT2 group (no bleaching+5% procyanidins for 5 min), WT2a group (no bleaching+5% procyanidins for 5 min+aging), C group (carbamide peroxide+deionized water), Ca group (carbamide peroxide+deionized water+aging), CT1 group (carbamide peroxide+5% procyanidins for 1 min), CT1a group (carbamide peroxide+5% procyanidins for 1 min+aging), CT2 group (carbamide peroxide+5% procyanidins for 5 min), and CT2a group (carbamide peroxide+5% procyanidins for 5 min+aging). The bond strength to composite resin was measured by universal mechanical testing machine, microstructure and the nanoleakages were measured by scanning electron microscope immediately or after the thermal cycling aging test.@*Results@#The immediate bond strength of the bleached groups pretreated with procyanidins for 1 min (P<0.001) and 5 min (P<0.001) was higher than that of Group C, and the difference was statistically significant. Meanwhile, there was no statistically significant difference between Group CT1 and Group CT2 (P = 1.000). After the thermal cycles, the bond strength of each group declined. The differences between Group W and Group Wa (P<0.001) and Group C and Group Ca (P<0.001) were statistically significant, but no significant differences between Group CT1 and Group CT1a (P = 0.052) or Group CT2 and Group CT2a (P = 0.053) were found. The main effects of “aging” (P<0.001), “bleaching” (P<0.001) and “procyanidins” (P<0.001) and the second-order interaction effects of “bleaching * procyanidins” (P = 0.008), “bleaching * aging” (P = 0.024), and “aging * procyanidins” (P<0.001) were statistically significant. SEM observations showed that the hybrid layers in Groups C, CT1 and CT2 were not clear, and the hybrid layers in Groups Ca, CT1a and CT2a were partially destroyed and disintegrated. Under backscattering mode, it was observed that there were a large number of silver nitrate particles in the hybrid layer of Group Ca, and the residual silver ions in the hybrid layer of Groups CT1a and CT2a were decreased. @*Conclusion@# Pretreatment with 5% procyanidins for 1 min can improve the immediate bond strength of dentin bleached by carbamide peroxide to composite resin and maintain bonding durability.

Dental and composite resin discoloration induced by different hydraulic calcium silicate-based cements: two-year in vitro assessment

Abstract Few long-term studies assess the discoloration induced by hydraulic calcium silicate-based cement on dental structures. In addition, as far as we know, no long-term study has assessed the discoloration induced by these cement on composite resin. Objective This in vitro study aimed to assess, during a period of two years, the discoloration potential of different hydraulic calcium silicate-based cements (hCSCs) on the enamel/dentin structure and composite resin restoration. Methodology A total of 40 enamel/dentin discs were obtained from bovine incisors, and 40 composite resin discs (10 mm in diameter × 2 mm thick) were fabricated. A 0.8 mm-deep cavity was made in the center of each disc and filled with the following hCSCs (n=10): Original MTA (Angelus); MTA Repair HP (Angelus); NeoMTA Plus (Avalon); and Biodentine (Septodont). An initial color measurement was performed (T0 - baseline). After 7, 15, 30, 45, 90, 300 days, and two years, new color measurements were performed to determine the color (ΔE00), lightness (ΔL'), chroma (ΔC'), hue differences (ΔH'), and whiteness index (WID). Results For enamel/dentin, the ΔE00 was significant among groups and periods (p<0.05). NeoMTA Plus had the greatest ΔE00. The NeoMTA Plus group had the greatest ΔE00 after two years for composite resin. Significant reduction in lightness was observed for all groups after two years (p<0.05). The most significant WID values were observed after 30 days for Biodentine (enamel/dentin) and MTA Repair HP groups (composite resin) (p<0.05). Conclusions The hCSCs changed the colorimetric behavior of both substrates, leading to greater darkening over time. The Bi2O3 in the Original MTA seems relevant in the short periods of color change assessment.

Grado de microfiltración en ionómero de vidrio y resina compuesta nanoparticulada en lesiones cervicales no cariosas / Degree of microleakage in glass ionomer and nanoparticulate composite resin in non-carious cervical lesions

Introducción: El grado de microfiltración en el ionómero de vidrio y la resina compuesta nanoparticulada en lesiones cervicales no cariosas es de gran importancia para elegir el material restaurador más adecuado para cada caso clínico. Objetivo: Describir el grado de microfiltración en ionómero de vidrio y resina compuesta nanoparticulada en lesiones cervicales no cariosas. Métodos: Se realizó una revisión bibliográfica, correspondiente al nivel exploratorio, en busca de responder cinco preguntas científicas sobre el tema. Se identificaron 62 artículos de las bases de datos de Google Académico o Scopus entre 2015 y 2022. Resultados: Los estudios consultados sugieren que la resina compuesta nanoparticulada es una opción de restauración efectiva y estética en odontología, especialmente en casos de cavidades de alta carga mecánica y estética dental. Los estudios de casos que se revisan demuestran que el grado de microfiltración en las lesiones cervicales no cariosas puede ser significativamente mayor en las restauraciones con ionómero de vidrio en comparación con las resinas compuestas nanoparticuladas. Conclusiones: Se concluye que el elemento fundamental en el tratamiento es realizar un correcto diagnóstico, determinando las necesidades para mejorar la salud dental y realizar una correcta planificación, por lo que es necesario conocer los diferentes tipos de tratamientos con la finalidad de seleccionar el más adecuado, que cumpla con las características biológicas, mecánicas y estéticas, ya que uno de los objetivos fundamentales de cualquier tratamiento es devolver la función y la estética de modo satisfactorio y con la mayor durabilidad posible.

Introduction: The degree of microleakage in glass ionomer and nanoparticulated composite resin in non-carious cervical lesions is of great importance for choosing the most suitable restorative material for each clinical case. Objective: To describe the degree of microleakage in glass ionomer and nanoparticulated composite resin in non-carious cervical lesions. Methods: A literature review, corresponding to the exploratory level, was carried out to answer five scientific questions on the subject. Sixty-two articles were identified from Academic Google or Scopus databases between 2015 and 2022. Results: The studies consulted suggest that nanoparticulated composite resin is an effective and esthetic restorative option in dentistry, especially in cases of cavities with high mechanical load and dental esthetics. The case studies reviewed demonstrate that the degree of microleakage in non-carious cervical lesions can be significantly higher in glass ionomer restorations compared to nanoparticulated composite resins. Conclusions: It is concluded that the fundamental element in treatment is to carry out a correct diagnosis, determining the needs to improve dental health and to carry out correct planning, so it is necessary to know the different types of treatments with the aim of selecting the most suitable one, which complies with the biological, mechanical and esthetic characteristics, since one of the fundamental objectives of any treatment is to restore function and esthetics in a satisfactory way and with the greatest possible durability.

Can composite packaging and selective enamel etching affect the clinical behavior of bulk-fill composite resin in posterior restorations? 24-month results of a randomized clinical trial

Abstract Objectives This is a double-blind, split-mouth, randomized clinical study that aims to evaluate the influence of bulk-fill composite packaging presented in syringes (BSy) and capsules (BCa), and the effect of selective enamel etching (SEE) on the clinical performance of class I and II bulk-fill resin composite restorations after 24 months. Methodology A total of 295 class I or class II restorations were performed on 70 patients. One universal adhesive was applied in all restorations. SEE was used in 148 restorations and self-etching mode (SET) in 147 restorations. After the adhesive application, cavities were restored with Filtek Bulk-fill Posterior Restorative in syringes (BSy), Filtek One Bulk-fill in capsules (BCa), or Filtek Supreme Ultra in syringes with the incremental technique (In). All restorations were evaluated using the FDI criteria after one week and after six, 12, and 24 months. Kaplan-Meier survival analysis and Pearson's Chi-square test were used (α=0.05) for statistical analysis. Results After 24 months, 62 patients were evaluated and four restorations were lost due to fracture (one for SEEBSy, two for SEEIn, and one for SETIn). No significant differences in the fracture and retention rate were found between groups (p>0.05). SEE showed significantly fewer marginal adaptation defects than SET (p<0.05). BCa and BSy groups showed fewer marginal discrepancies compared to In (p<0.05). Restorations performed with BCa showed less color mismatch than BSy or In (p<0.05). Conclusion Although all restorations exhibited satisfactory clinical performance after 24 months of clinical service, the clinical behavior of class I and II restorations' improved when performed with a bulk-fill composite in capsules, mainly when associated with a universal adhesive applied with SEE.

Stress distribution in occlusal veneers with different finish lines when applying vertical and tangential forces / Distribución de estrés en carillas con diferentes líneas de terminación aplicando fuerzas verticales y tangenciales

Abstract To evaluate stress distribution when applying vertical and tangential forces to 1mm thick occlusal veneers with different finish lines preparations, using the finite element method. One extracted third molar was prepared for occlusal veneers, firstly without any bevel. It was scanned in order to design two groups of lithium disilicate (G1A, G2A) and composite resin (G1B, G2B) occlusal veneers. Then, the third molar preparation was modified, beveling the finish line and it was subsequently scanned again to design the occlusal veneer groups with bevel (LD: G3A, G4A and CR: G3B, G4B). The four groups were subjected to different forces (400 N vertical and 900 N tangential). At 400 N, the non-beveled veneers showed slightly higher Von Mises stress values (G1A: 783 MPa and G1B 736.5 MPa) than the beveled veneers (G3A: 685.7 MPa and G3B: 675.8 MPa). However, when 900 N tangential forces were applied, the beveled occlusal veneers showed higher Von Mises stress values (G4A: 4297 MPa and G4B: 4133 MPa) than the non-beveled occlusal veneers (G2A: 2581.1 MPa and G2B: 3519.1 MPa). Furthermore, it was observed that the tissue under the occlusal veneers with bevel showed higher Von Mises stress values than the models without any bevel. Beveled and non-beveled occlusal veneers of lithium disilicate and composite resin presented similar stress distribution values when vertical forces of 400 N were applied; whereas with tangential forces of 900 N applied near to the finish line, the beveled groups presented notably higher stress values than the non-beveled groups. However, both finish line preparations presented adequate values for possible clinical performance.

Resumen Evaluar la distribución de estrés al aplicar fuerzas verticales y tangenciales en carillas oclusales de 1mm de espesor con diferentes líneas de terminación marginal por el método de elementos finitos. Se preparó un tercer molar extraído para carilla oclusal, primero sin bisel. Se escaneó para diseñar dos grupos de carillas oclusales de disilicato de litio (G1A, G2A) y resina compuesta (G1B, G2B). Después, esta preparación molar fue modificada, biselando la línea de terminación y escaneándola nuevamente para diseñar los grupos de carillas oclusales con bisel (DL: G3A, G4A and RC: G3B, G4B). Los 4 grupos fueron sometidos a fuerzas diferentes (400 N vertical y 900 N tangencial). Con 400 N, las carillas sin bisel presentaron ligera mayor tensión de Von Mises (G1A: 783 MPa y G1B 736.5 MPa) que las carillas con bisel (G3A: 685.7 MPa y G3B: 675.8 MPa). De distinta forma, al aplicar fuerzas tangenciales de 900 N, las carillas oclusales con bisel presentaron mayor tensión de Von Mises (G4A: 4297 MPa y G4B: 4133 MPa) que las carillas oclusales sin bisel (G2A: 2581.1 MPa y G2B: 3519.1 MPa). Además, se observó que los tejidos subyacentes a las carillas oclusales con bisel, presentaron mayor tensión de Von Mises, frente a los modelos sin bisel. Las carillas oclusales con y sin bisel de disilicato de litio y resina compuesta presentaron una distribución de estrés similar con fuerzas verticales de 400 N, por otro lado, con fuerzas tangenciales de 900 N, los grupos con bisel presentaron notablemente mayor tensión que los grupos sin bisel. Sin embargo, ambos diseños de terminación marginal presentaron valores adecuados para un posible desempeño clínico.

Effect of a polymerization inhibitor on the chemomechanical properties and consistency of experimental resin composites

Abstract This study investigated the effect of butylated hydroxytoluene (BHT) inhibitor on degree of conversion (DC), flexural strength (FS), flexural modulus (FM), Knoop microhardness (KH), microhardness reduction (HR), and consistency of experimental resin composites at different BHT concentrations: C0 (control-0%); C0.01 (0.01%); C0.025 (0.025%); C0.05 (0.05%); C0.1 (0.1%); and C0.5 (0.5%). For the consistency, the composites were tested immediately after being exposed to a dental chair headlight (0, 20, 40 and 60 s). Data concerning DC, FS, FM, KH, and HR were submitted to one-way ANOVA, while the consistency data was submitted to 2-way ANOVA; mean values were then compared (Tukey's test; α=0.05). The KH, FS and FM analyses showed no significant difference among the composites tested. For DC, C0 showed the highest mean value (74.2%) and differed only from C0.5 (67.2%). For HR, C0.5 showed the lowest mean (13.09%) value and differed from C0 (26.4%) and C0.01 (24.87). The consistency analysis showed no difference among C0.05, C0.1 and C0.5, considering 0 and 20 s of light exposure, while C0 (14.07 mm), C0.01 (13.97 mm), and C0.025 (14.18 mm) showed higher mean values at 0 s when compared to 20 s (12.67, 12.77 and 13.05 mm, respectivelly). Polymerization occurred within 40 s of light exposure for C0, C0.01, C0.025, and C0.05 and within 60 s for C0.1. In conclusion, the BHT concentrations had no significant influence on FS, FM and KH. The higher the BHT concentration, the longer was its handling time under light, with a significant improvement in the HR, but a decrease in DC. Therefore, BHT at 0.1% showed the best outcomes concerning all the BHT concentrations tested.

Resumo O objetivo foi investigar o efeito do inibidor de polimerização BHT no grau de conversão (GC), resistência à flexão (RF), módulo de flexão (MF), microdureza Knoop (KH) e redução da microdureza (RKH), e consistência de um compósito experimental contendo diferentes concentrações de BHT (% em peso): C0 - controle (0%); C0,01 (0,01%); C0,025 (0,025%); C0,05 (0,05%); C0,1 (0,1%); e C0,5 (0,5%). Para o teste de consistência, os compósitos foram testados imediatamente após serem expostos à luz de um refletor odontológico por 0, 20, 40 e 60 s. Os dados relativos a GC, RF, MF, KH e RKH foram submetidos a one-way ANOVA, enquanto os dados de consistência foram submetidos a two-way ANOVA; os valores médios foram comparados (teste de Tukey; α = 0,05). As análises de KH, RF e MF não mostraram diferença significativa entre os compósitos testados. Para GC, C0 apresentou o maior valor médio e diferiu apenas de C0,5. Para a RKH, C0,5 apresentou o menor valor médio e diferiu de C0 e C0,01. A análise de consistência não mostrou diferença entre C0,05, C0,1 e C0,5, considerando-se 0 e 20 s de exposição à luz, enquanto C0, C0,01 e C0,025 apresentaram maiores valores médios a 0 s quando comparados a 20 s. A polimerização ocorreu dentro de 40 s de exposição à luz para C0, C0.01, C0.025 e C0.05 e dentro de 60 s para C0.1. Em conclusão, as concentrações de BHT não tiveram influência significativa sobre RF, MF e KH. Quanto maior a concentração de BHT, maior o tempo de manuseio sob luz, com melhora significativa da RKH, mas diminuição da GC. Portanto, o compósito contendo 0,1 % de BHT apresentou os melhores resultados entre as demais concentrações testadas.

No-Prep semidirect composite resin veneer. A Step-by-Step case report in a deciduous canine with a one-year follow-Up / Carilla de resina semidirecta sin preparación. Un reporte paso a paso en un canino deciduo con seguimiento de un año

Abstract The presence of deciduous canines in adulthood may be of aesthetic concern for patients. Many clinical alternatives include surgical and orthodontic treatment. Since patients search for highly esthetic results and more conservative alternatives, the present clinical report describes a treatment for deciduous canine through an indirect composite resin veneer and an indirect composite resin fragment restoration in a premolar to improve esthetic outcomes with a one-year follow up.

Resumen La presencia de caninos deciduos en adultos puede ser de preocupación estética por parte de los pacientes. Diversas alternativas clínicas pueden incluir tratamientos quirúrgicos y ortodóncicos. Desde que los pacientes buscan por resultados de alta estética y cada vez más conservadores, es que el presente caso clínico describe el tratamiento de un canino deciduo mediante una carilla indirecta de resina compuesta junto a un fragmento indirecto de resina de un premolar con el fin de mejorar los resultados estéticos, y con un año de seguimiento.

¿La glicerina influye en la estabilidad del color de la resina compuesta? / Does glycerin influence the color stability of composite resin?

Introducción: El efecto del oxígeno sobre la superficie de las resinas al momento de la fotopolimerización origina una capa que es susceptible a los pigmentos. El uso de la glicerina puede bloquear este efecto. Objetivo: Determinar si existe diferencia en la estabilidad del color de la resina compuesta nano-híbrida sometida a un agente colorante, al aplicar o no la glicerina. Métodos: 60 discos de resina se dividieron en Grupo 1 (sin glicerina) y Grupo 2 (con glicerina). La fotopolimerización se realizó por 20 s con la lámpara LED Bluephase®N. Se realizó la primera medición del color con el espectrofotómetro Easyshase®V y se registraron los valores arrojados para L* (luminosidad), a* (eje rojo-verde) y b* (eje azul-amarillo). Posterior a la inmersión por 1 mes de las muestras en Coca-Cola®, manteniéndolas en una incubadora a 37 ºC, se realizó la segunda medición del color. Se procesaron los datos estadísticamente con la prueba t de Student para determinar las variaciones en la estabilidad del color de ambos grupos y compararlos entre sí. Resultados: En todos los especímenes del experimento existió alteración en la estabilidad del color de la resina. La media de la distancia entre el color inicial y el color final del Grupo 1 fue de ΔE = 6,91, mientras en el Grupo 2 fue ΔE = 3,74. Se halló diferencia estadísticamente significativa entre ambos grupos analizados (p < 0,001). Conclusiones: La glicerina es una sustancia efectiva para bloquear el efecto del oxígeno en la superficie de la resina y evitar la formación de la capa inhibida de oxígeno, aumentando la estabilidad del color de la resina compuesta nano-híbrida(AU)

Introduction: The effect of oxygen on the surface of resins at the moment of photopolymerization creates a layer which is susceptible to pigments. The use of glycerin may block this effect. Objective: Determine whether there is a difference in the color stability of nanohybrid composite resin subjected to a coloring agent when glycerin is either applied or not applied. Methods: Sixty resin disks were distributed into Group 1 (without glycerin) and Group 2 (with glycerin). Photopolymerization was performed for 20 s with a Bluephase®N LED lamp. The first color measurement was taken with an Easyshase®V spectrophotometer, recording the values obtained for L* (luminosity), a* (red-green axis) and b* (blue-yellow axis). The second color measurement was taken after immersion of the samples for one month in Coca-Cola®, maintaining them in an incubator at 37ºC. Statistical data analysis was performed with Student's t test to determine the color stability changes occurring in the two groups and compare them. Results: Color stability changes were observed in all the resin samples. Mean distance between initial and final color was ΔE = 6.91 in Group 1 and ΔE = 3.74 in Group 2. A statistically significant difference was found between the two groups analyzed (p < 0.001). Conclusions: Glycerin is an effective substance to block the effect of oxygen on the resin surface, preventing the formation of an oxygen-inhibited layer and raising the color stability of the nanohybrid composite resin(AU)

The effects of different antioxidant agents on the microtensile bond strength of composite resin to bleached Enamel / Efecto de diferentes agentes antioxidantes en la resistencia a la microtracción de la resina compuesta al esmalte blanqueado

Abstract The objective of this in vitro study is to examine the effect of antioxidants on the bonding strength of composite resin to bleached enamel. One hundred twenty non decay teeth were used in this study. Specimens were cut from the enamel cement junction. Then the specimens were randomly assigned into two groups-office bleaching and home bleaching. Bleaching antioxidants were applied to the first 12 subgroups. The specimens in the remaining 12 groups were kept in artificial saliva for 14 days and antioxidants were applied. Composite resin restoration was applied to all specimens. A cutting device was employed to obtain six specimens (0.9mm) from each tooth, and the microtensile bond strength (μTBS) test was performed. Data were analyzed using one-way ANOVA, the paired t-test, and Duncan's post hoc test (p=0.05). In office bleaching specimens, immediate antioxidant application increased the μTBS values (p0.05). Mean μTBS values in the groups to which antioxidants were applied two weeks after home bleaching were higher than those in the groups in which antioxidants were applied immediately. The use of antioxidants after bleaching may increase the MTBS value. The clinician should take this into account especially in immediate restoration applications after bleaching.

Resumen El objetivo de este estudio in vitro fue examinar el efecto de los antioxidantes sobre la resistência adhesiva de la resina compuesta al esmalte blanqueado. En este estudio se utilizaron ciento veinte dientes sin caries. Se cortaron especímenes a nivel de la unión esmalte-cemento. A continuación, los especímenes se asignaron aleatoriamente a dos grupos: blanqueamiento en el consultorio y blanqueamiento en casa. Se aplicaron antioxidantes de blanqueamiento a los primeros 12 subgrupos. Los especímenes de los 12 grupos restantes se mantuvieron en saliva artificial durante 14 días y se aplicaron antioxidantes. Se aplicó una resina compuesta a todos los especímenes empleando un dispositivo de corte para obtener seis especímenes (0,9mm) de cada diente, y se realizó la prueba de resistencia a la adhesión por microtensión (μTBS). Los datos se analizaron mediante un ANOVA de una vía, la prueba t pareada y la prueba post hoc de Duncan (p=0,05). En las muestras de blanqueamiento de oficina, la aplicación inmediata de antioxidantes aumentó los valores de μTBS (p0,05). Los valores medios de μTBS en los grupos a los que se aplicaron antioxidantes dos semanas después del blanqueo en casa fueron mayores que los de los grupos en los que se aplicaron antioxidantes inmediatamente. El uso de antioxidantes después del blanqueamiento puede aumentar el valor de μTBS. El clínico debe tenerlo en cuenta, especialmente en las aplicaciones de restauración inmediatas tras el blanqueamiento.

X-Ray Microtomography Analysis of Gaps and Voids in the Restoration of Non-Carious Cervical Lesions with Different Composite Resins

Context (Background): Resin composites are the most widely used material for restoring cervical defects. However, the high failure rate of these restorations is still a concern. Aims: The aim of this in vitro study was to evaluate, using microtomography (?CT), the interfacial gap and voids formation in Class V cavities in premolars restored with materials with lower polymerization shrinkage combined with different restorative techniques. Settings and Design: Cervical defects were created in 30 intact premolar and were randomly distributed to be restored by one of the following techniques (n = 6): Composite resin with two increments (CR), organic modified polymer (ORMOCER) with single (OR1) or two increments (OR2, or low viscosity bulk?fill composite resin with single (BF1) or two increments (BF2). Methods and Material: Each tooth was scanned before filling to determine the volume of interest (VOI) to be applied in the second ?CT after restoration and to control the cavity volume among the groups. In the ?CT after filling, the volume of interfacial gaps and voids was calculated for each group. Statistical Analysis: The groups were compared using one?way and Tukey HSD post hoc test (? = 0.05). Results: It was possible to identify higher gap formation in the OR1 group and higher void formation in CR group (P < 0.05). OR2 group showed better results than the group with one increment. BF2 showed the best filling capacity. Conclusions: It was possible to conclude that the material and the number of increments directly influenced the internal adaptation and voids formation of Class V restorations.

A comparative evaluation of gingival microleakage and internal voids in Class II composite restoration with two different lining techniques An in vitro study

Aim: The aim of this study was to evaluate the gingival microleakage and internal voids in Class II composite restoration restored with precure and co-cure lining techniques using stereomicroscopic method. Materials and Methods: Forty-five freshly extracted permanent multirooted human molar teeth were collected and used in the study. After surface debridement and scaling of all teeth, standard Class II mesio-occlusal cavities were prepared. Forty-five samples were randomly divided into three experimental groups (n = 15), and filled according to manufacturer's instructions. Group I was precure group, Group II was co-cure group, and Group III was only bulk fill. The finishing and polishing of the restorations was done after 24 h. Then, all the specimens were subjected to thermocycling for 500 cycles. The gingival microleakage and internal voids of all the groups were evaluated using dye penetration method. Samples were then sectioned and examined under the stereomicroscope at ×40. Readings obtained were subjected to statistical analysis using SPSS ver 20.0 (IBM Corp, ARMONK USA) and Chi-square test. Results: The statistical analysis revealed that extent of microleakage was maximum in Group II (co-cure), followed by Group III (only bulk fill) and Group I (precure). The gingival voids were maximum in Group III (only bulk fill), minimum in Group II (co-cure), and least in Group I (precure). The cervical voids were maximum in Group II (co-cure) and Group III (only bulk fill), followed by Group I (precure). The occlusal voids were maximum in Group II (co-cure) and similar in Group I (precure) and Group III (only bulk fill). Conclusion: The precure lining technique was better than co-cure lining technique in terms of both microleakage and internal voids.

Effect of handling, time of use and photoactivation on the contamination of dental composite resins

This study evaluated the effect of contamination of composite resins (CRs) handled by undergraduate students during restorative procedures, varying the time (baseline, 30 days and 60 days) and experimental condition (before and after handling, contamination with saliva [positive control] and photoactivation). Eight CR tubes were randomly distributed at the dental clinic and the samples were organized into four groups: CR fragments collected before (GB) and after (GA) the restorative procedure; CR fragments contaminated with saliva (GS) and photoactivated (GP) both collected after the procedure. These 4 groups were evaluated in 3 different times: baseline (after sealing), 30 days and 60 days of use of the CR. Samples that had positive turbidity in Brain HeartInfusion (BHI) broth were sown in BHI and Sabouraud Dextrose (SB) agars for subsequent counting of Colony Forming Units (CFU mL-1). The results showed that the handling was responsible for increasing contamination (p < 0.05) at the baseline (GB [n = 0] and GA [n = 3]), as well as after 30 (GB [n = 1] and GA [n = 6]) and 60 (GB [n = 1] and GA [n = 5]) days of use. Photoactivation was responsible for the reduction for microorganisms in T0 and T60. Additionally, the time use and conservation did not influencethe contamination of CRs. Handling was responsible for the increase of contamination of CR, the photoactivation seems to reduce the number of viable microorganisms and the time of use seems not to potentiate the effect of tube contamination.

Evaluation of the marginal adaptation of class II restorations carried out in a Faculty in the State of Espírito Santo / Avaliação da adaptação marginal das restaurações classe II realizadas em uma Faculdade no Estado do Espírito Santo

Introduction: composite resins are materials widely used for Class II restorations, to restore the anatomization of the dental element. However, there are several factors that can interfere with the quality of a good restoration. Objective: the objective of the present study is to carry out a retrospective evaluation of the clinical performance of Class II restorations performed by undergraduate students of Dentistry at the Escola São Francisco de Assis (ESFA), and to identify the main errors. Material and method: we selected the medical records of patients treated in the disciplines of Dentistry II, Integrated I and II in the Dentistry clinic at ESFA, which presented detailed information on the Class II procedure, as well as initial radiographic examinations, using the FDI method. The sample consisted of 33 medical records that included 72 teeth. Result: it was observed that more than 80% of the restorations were classified as acceptable. And, only 19.44% of the restorations were unacceptable, failing due to functional and biological properties. Conclusion: it was found that undergraduate students in Dentistry at ESFA, who are guided by professors to perform treatments following pre-established clinical protocols, are capable of carrying out quality restorative procedures.

Introdução: as resinas compostas são materiais muito utilizados para restaurações Classe II, com função de restabelecer a anatomização do elemento dental. No entanto, diversos são os fatores que podem interferir na qualidade de uma boa restauração. Objetivo: o objetivo do presente estudo é realizar uma avaliação retrospectiva do desempenho clínico de restaurações Classe II executadas por alunos da graduação de Odontologia da Escola São Francisco de Assis (ESFA) e identificar as principais falhas cometidas. Material e método: foram selecionados os prontuários dos pacientes atendidos nas disciplinas de Dentística II, Integrada I e II na clínica de Odontologia da ESFA, que apresentaram as informações detalhadas do procedimento de Classe II, bem como exames radiográficos iniciais, usando o método FDI. A amostra foi composta por 33 prontuários que incluíam 72 dentes. Resultado: observou-se que mais de 80% das restaurações foram classificadas como aceitáveis. Visto que, apenas 19,44% das restaurações estiveram inaceitáveis, pecando para as propriedades funcionais e biológicas. Conclusão: constatou-se que os alunos da graduação em Odontologia da ESFA, os quais são orientados por professores a realizar tratamentos seguindo protocolos clínicos pré-estabelecidos, são capazes de confeccionar procedimentos restauradores de qualidade.

A new preheating thermoviscous composite for restoration of non-carious cervical lesions: a 6-month randomized clinical trial / Um novo compósito termoviscoso de pré-aquecimento para restauração de lesões cervicais não cariosas: ensaio clínico randomizado de 6 meses

Objetivo: Este ensaio clínico randomizado, duplo-cego e boca dividida avaliou o desempenho clínico de um novo compósito termoviscoso com pré-aquecimento (PHT) em comparação com uma resina composta sem aquecimento (NHT) em restaurações de lesões cervicais não cariosas (LCNCs) durante um período de 6 meses. Material e Métodos: 120 restaurações foram realizadas em LCNCs com dois materiais restauradores (n = 60). Após a profilaxia, os dentes foram isolados com isolamento de fio retrator/rolos de algodão e um adesivo universal foi aplicado na estratégia de condicionamento seletivo do esmalte. Para o grupo PHT o aquecimento foi realizado a 68°C usando um aquecidor de bancada por 3 min. Por outro lado, para o grupo NHT, nenhum aquecimento foi aplicado. Ambos os materiais restauradores foram colocados no dispensador de cápsulas e inseridos nas LCNCs. Após 6 meses, o desempenho clínico das restaurações foi avaliado de acordo com os critérios FDI. A análise estatística foi realizada com teste Qui-quadrado para todos parâmetros da FDI (α = 0,05). Resultados: Apenas três restaurações no grupo NHT foram perdidas/fraturadas após seis meses de acompanhamento. As taxas de retenção (intervalo confiança 95%) por seis meses foram de 97,5% (88,6% - 99,0%) para o grupo NHT e 100% (93,9% - 100%) para o grupo PHT (p > 0,05). Vinte e duas restaurações (8 para NHT e 14 para PHT) apresentaram pequenos defeitos de adaptação marginal aos seis meses de acompanhamento (p > 0,05). Vinte e seis restaurações apresentaram alguma retenção de biofilme aos seis meses de acompanhamento (11 para NHT e 15 para PHT; p > 0,05). Em relação a todos os outros parâmetros de FDI avaliados, todas as restaurações foram consideradas clinicamente aceitáveis. Conclusão: O desempenho clínico do novo compósito termoviscoso de pré-aquecimento mostrou-se promissor após 6 meses de avaliação clínica quando aplicado em LCNCs.(AU)

Objective: This double-blind, split-mouth randomized clinical trial evaluate the clinical performance of a new preheating (PHT) thermoviscous composite compared to a non-heating (NHT) composite resin in restorations of non-carious cervical lesions (NCCLs) over a period of 6-month. Material and Methods: 120 restorations were performed on NCCLs with two restorative materials (n = 60). After prophylaxis, the teeth were isolated with retraction cord isolation/cotton rolls and one universal adhesive was applied in the selective enamel etching strategy. For the PHT group heating was carried out at 68°C using a heater bench for 3 min. On the other side, for the NHT group, no heating was applied. Both restorative materials were placed in the caps dispenser and inserted in the NCCLs. The restorations were evaluated after 6-month of clinical performance according to the FDI criteria. Statistical analysis was performed with Chi-square test for all FDI parameters (α = 0.05). Results: Three restorations only in the NHT group were lost/fractured after six months follow-up. The retention rates (confidential interval 95%) for six months were 97.5% (88.6% - 99.0%) for the NHT group and 100% (93.9% - 100%) for the PHT group (p > 0.05). Twenty-two restorations (8 for NHT and 14 for PHT) presented small marginal adaptation defects at the six-months follow-up (p > 0.05). Twenty-six restorations were found to have biofilm retention in the six-month recall (11 for NHT and 15 for PHT; p > 0.05). Regarding all others FDI parameters evaluated, all restorations were considered clinically acceptable. Conclusion: The clinical performance of the new preheating thermoviscous was found to be promise after 6-month of clinical evaluation when applied in NCCLs (AU)